321 ruostumaton teräsnauha
Ruostumattomasta teräslevystä valmistettu Baogu-laatu
| Tyyppi | Arvosana | Arvosana | Kemiallinen komponentti % | ||||||||||
| C | Cr | Ni | Mn | P | S | Mo | Si | Cu | N | Muut | |||
| Austeniittista | 201 | SUS201 | ≤0,15 | 16.00-18.00 | 3.50-5.50 | 5.50 - 7.50 | ≤0,060 | ≤0,030 | - | ≤1.00 | - | ≤0,25 | - |
| 202 | SUS202 | ≤0,15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 | ≤0,060 | ≤0,030 | ≤1.00 | - | ≤0,25 | － | ||
| 301 | 1.431 | ≤0,15 | 16.00-18.00 | 6.00-8.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | ≤0,10 | - | |
| 304 | 1.4301 | ≤0,07 | 17.00-19.00 | 8.00-10.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 304 litraa | 1,4307 | ≤0,030 | 18.00-20.00 | 8.00-10.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 304H | 1,4948 | 0,04-0,10 | 18.00-20.00 | 8.00-10.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 309 | 1,4828 | ≤0,20 | 22.00-24.00 | 12.00-15.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 309S | * | ≤0,08 | 22.00-24.00 | 12.00-15.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 310 | 1,4842 | ≤0,25 | 24.00-26.00 | 19.00-22.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1,50 | - | - | - | |
| 310S | * | ≤0,08 | 24.00-26.00 | 19.00-22.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1,50 | - | - | - | |
| 314 | 1,4841 | ≤0,25 | 23.00-26.00 | 19.00-22.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | 1.50-3.00 | - | - | - | |
| 316 | 1.4401 | ≤0,08 | 16.00-18.50 | 10.00-14.00 | ≤2.00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1.00 | - | - | - | |
| 316 litraa | 1.4404 | ≤0,030 | 16.00-18.00 | 10.00-14.00 | ≤2.00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1.00 | - | - | - | |
| 316Ti | 1,4571 | ≤0,08 | 16.00-18.00 | 10.00-14.00 | ≤2.00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1.00 | - | 0.1 | Ti5(C+N)-0,70 | |
| 317 | * | ≤0,08 | 18.00-20.00 | 11.00-15.00 | ≤2.00 | ≤0,045 | ≤0,030 | 3.00-4.00 | ≤1.00 | - | 0.1 | - | |
| 317 litraa | 1,4438 | ≤0,03 | 18.00-20.00 | 11.00-15.00 | ≤2.00 | ≤0,045 | ≤0,030 | 3.00-4.00 | ≤1.00 | - | 0.1 | - | |
| 321 | 1,4541 | ≤0,08 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | Ti5(C+N)-0,70 | |
| 321H | * | 0,04-0,10 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | Ti5(C+N)-0,70 | |
| 347 | 1.455 | ≤0,08 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | Nb≥10*C-1,10 | |
| 347H | 1,494 | 0,04-0,10 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | Nb≥10*C-1,10 | |
| xm-19 | Nitronic50 | ≤0,06 | 20.50-23.50 | 11.50-13.50 | 4,0-6,0 | ≤0,045 | ≤0,030 | 1.50-3.00 | ≤1.00 | - | 0,2-0,4 | Nb:0,10-0,30 V:0,10-0,30 | |
| 904L | N08904 | ≤0,02 | 19,0-23,0 | 23,0-28,0 | 4,0-5,0 | ≤0,045 | ≤0,035 | ≤1.00 | 0.1 | Cu: 1,0-2,0 | |||
| Duplex | 2205 | S32205 | ≤0,03 | 22,0-23,0 | 4,5-6,5 | ≤2.00 | ≤0,030 | ≤0,020 | 3,0-3,5 | ≤1.00 | - | 0,14-0,20 | |
| 2507 | S32750 | ≤0,03 | 24,0-26,0 | 6,0-8,0 | ≤1,20 | ≤0,035 | ≤0,020 | 3,0-5,0 | ≤0,80 | 0.5 | 0,24-0,32 | ||
| * | S32760 | ≤0,03 | 24,0-26,0 | 6,0-8,0 | ≤1.00 | ≤0,030 | ≤0,010 | 3,0-4,0 | ≤1.00 | 0,5-1,00 | 0,2-0,3 | ||
| 2304 | S32304 | ≤0,03 | 21.5-24.5 | 3,0-5,5 | ≤2,50 | ≤0,040 | ≤0,030 | 0,05-0,6 | ≤1.00 | 0,05-0,6 | 0,05-0,2 | ||
| 329 | 1.446 | ≤0,08 | 23.00-28.00 | 2.00-5.00 | ≤1.00 | ≤0,040 | ≤0,030 | 1.00-2.00 | ≤0,75 | - | - | ||
| Ferriitti | 409 | S40900 | ≤0,03 | 10.50-11.70 | 0.5 | ≤1.00 | ≤0,040 | ≤0,020 | - | ≤1.00 | - | ≤0,030 | Ti6(C+N)-0,50 Nb: 0,17 |
| 430 | 1Cr17 | ≤0,12 | 16.00-18.00 | - | ≤1,0 | ≤0,040 | ≤0,030 | - | ≤1,0 | - | - | - | |
| 444 | S44400 | ≤0,025 | 17.50-19.50 | 1 | ≤1.00 | ≤0,040 | ≤0,030 | 1,75-2,5 | ≤1.00 | - | 0,035 | Ti+Nb: 0,2+4(C+N)-0,80 | |
| 446 | S44600 | ≤0,20 | 23.00-27.00 | 0,75 | ≤1,5 | ≤0,040 | ≤0,030 | 1,50-2,50 | ≤1.00 | - | ≤0,25 | - | |
| Martensiitti | 410 | 1Cr13 | 0,08-0,15 | 11.50-13.50 | 0,75 | ≤1.00 | ≤0,040 | ≤0,030 | - | ≤1.00 | - | - | - |
| 410S | * | ≤0,080 | 11.50-13.50 | 0.6 | ≤1.00 | ≤0,040 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 416 | Y1Cr13 | ≤0,15 | 12.00-14.00 | 3) | ≤1,25 | ≤0,060 | ≥0,15 | - | ≤1.00 | - | - | - | |
| 420 | 2Cr13 | ≥0,15 | 12.00-14.00 | - | ≤1.00 | ≤0,040 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 420J2 | 3Cr13 | 0,26-0,35 | 12.00-14.00 | - | ≤1.00 | ≤0,040 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 431 | 1Cr17Ni2 | ≤0,20 | 15.00-17.00 | 1,50-2,50 | ≤1.00 | ≤0,040 | ≤0,030 | - | ≤0,80 | - | - | - | |
| 440C | 11Cr17 | 0,95-1,20 | 16.00-18.00 | - | ≤1.00 | ≤0,040 | ≤0,030 | 0,75 | ≤1.00 | - | - | - | |
| PH | 630 | 17-4PH | ≤0,07 | 15.00-17.50 | 3.00-5.00 | ≤1.00 | ≤0,035 | ≤0,030 | - | ≤1.00 | 3.00-5.00 | - | Nb 0,15-0,45 |
| 631 | 17-7PH | ≤0,09 | 16.00-18.00 | 6.50-7.50 | ≤1.00 | ≤0,035 | ≤0,030 | - | ≤1.00 | ≤0,50 | - | Al 0,75-1,50 | |
| 632 | 15-5PH | ≤0,09 | 14.00-16.00 | 3.50-5.50 | ≤1.00 | ≤0,040 | ≤0,030 | 2.00-3.00 | ≤1.00 | 2,5-4,5 | - | Al 0,75-1,50 | |
Kuvaus
321 ruostumaton teräsnauha on austeniittisen ruostumattoman teräksen tyyppi, jolla on alhainen hiilipitoisuus ja hyvä korroosionkestävyys monissa syövyttävissä ympäristöissä.321 tarjoaa erinomaisen hitsattavuuden, hyvän työstettävyyden ja erinomaiset valmistusominaisuudet.
321 ruostumatonta teräsnauhaa käytetään yleisesti kemianteollisuudessa, massa- ja paperiteollisuudessa, meri- ja offshore-koneteollisuudessa sekä elintarvike- ja juomateollisuudessa.
321 ruostumattomasta teräksestä valmistetun nauhan kestävyys on myös korkea kloridijännitekorroosiohalkeilua ja pistesyöpymistä vastaan.Se kestää myös suolahappoa korkeissa lämpötiloissa aina 250°C (480°F) asti.
ominaisuudet
Hyvä korroosionkestävyys: ruostumattomalla teräsnauhalla 321 on parempi korroosionkestävyys kuin 304- ja 316-tyypeillä ruostumattomilla teräksillä, mikä tekee siitä ihanteellisen käytettäväksi syövyttävissä ympäristöissä.
Erinomainen hitsattavuus: 321 ruostumaton teräsnauha voidaan hitsata kaikilla menetelmillä, mukaan lukien kaarihitsaus (TIG / GTAW), elektronisuihkuhitsaus (EBW / EFW), uppokaarihitsaus (SAW) ja lasersädehitsaus (LBIW).
Korkea lujuus: 321 ruostumattoman teräsnauhan lujuustasot ovat jopa 50 % korkeammat kuin 304 ruostumattomien terästen lujuustasot ja jopa 80 % korkeammat kuin 316 ruostumattomien terästen lujuustasot niiden lisääntyneen hiilipitoisuuden ja austeniittiraekoon vuoksi.